PEI 基礎(chǔ)創(chuàng)新塑料(美國) 1010 物性認證數(shù)據(jù)表
-
| 性能項目 |
測試條件 |
測試方法 |
數(shù)值/描述 |
單位 |
| 機械性能 |
拉伸強度(引張強度) |
|
ASTM D638/ISO 527 |
15200 |
kg/cm²(MPa)[Lb/in2] |
| 拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
| 拉伸屈服伸長率(延伸率) |
|
ASTM D638/ISO 527 |
7.0 |
% |
| 拉伸斷裂伸長率(延伸率) |
|
ASTM D638/ISO 527 |
60.0 |
% |
| 彎曲模量(彎曲彈性率) |
|
ASTM D790/ISO 178 |
60.0 |
kg/cm²(MPa)[Lb/in2] |
| 彎曲強度 |
|
ASTM D790/ISO 178 |
22000 |
kg/cm²(MPa)[Lb/in2] |
| 洛氏硬度 |
|
ASTM D785 |
109 |
|
| IZOD 缺口沖擊強度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
0.6 |
kg·cm/cm(J/M)ft·lb/in |
| 1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.27 |
|
| 成型收縮率 |
|
ASTM D955 |
|
% |
| 熔融指數(shù)（流動系數(shù)） |
200℃/5kg |
ASTM D1238/ISO 1133 |
|
g/10min |
| 220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
| 吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
0.250 |
% |
| 熱性能 |
熱變形溫度 |
退火 |
ASTM D648/ISO 75 |
405 66psi |
℃（H） |
| 未退火 |
ASTM D648/ISO 75 |
|
℃（H） |
| 維卡軟化點 |
|
ASTM D1525/ISO R306 |
426 |
℃（H） |
| 燃燒性（率） |
|
UL94 |
V-0 |
|
| 線性膨脹系數(shù) |
|
ASTM D696/ISO 11359 |
3 |
mm/mm.℃ |
| 電氣性能 |
介電常數(shù) |
100HZ |
ASTM D150/IEC 60250 |
3.15 |
|
| 1MHZ |
ASTM D150/IEC 60250 |
|
|
| 介電損耗 |
100HZ |
ASTM D150/IEC 60250 |
|
|
| 1MHZ |
ASTM D150/IEC 60250 |
|
|
| 體積電阻率 |
|
ASTM D257/IEC 60093 |
1E17 |
Ω.cm |
| 表面電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω |
| 耐電弧性 |
|
ASTM D495/IEC 60112 |
|
|
| 加工條件 |
干燥條件 |
|
|
|
|
| 加工溫度 |
射嘴 |
|
|
℃ |
| 料筒前段 |
|
|
℃ |
| 料筒中段 |
|
|
℃ |
| 料筒后段 |
|
|
℃ |
| 熔體溫度 |
|
|
|
℃ |
| 模具溫度 |
|
|
|
℃ |
| 壓力 |
注塑壓力 |
|
|
Mpa |
| 保壓壓力 |
|
|
Mpa |
| 背壓 |
|
|
Mpa |
| 螺桿轉(zhuǎn)速 |
|
|
|
rpm |
| 其他 |
備注 |
|
| 顏色 |
|
| 特性 |
|
| 用途 |
|
點擊圖片查看原圖
通過認證 